Customized C53-34 Alkyd Mica Ferric Oxide Paint From China

这里可以自定义设置

PRODUCT DESCRIPTION

This one-component product is mainly prepared by vegetable oil modified long-oil pentaerythritol resin, microscale flaky mica ferric oxide and aluminum powder.

This product features:

● High hardness

● Drying at ambient temperature

● Low permeability to water

● Long lifespan

● Great resistance to weathering, chalking, rust, corrosion and moisture

Typical Uses:

This product is widely used as intermediate coat for antirust purpose, such as:

● Steel structure

● Machinery

● Ships

● Bridges

● Gas storage tanks

● Containers

这里可以自定义设置

PRODUCT SELLING POINT

● High hardness, drying at ambient temperature

● Low permeability to water,long lifespan

● Great resistance to weathering, chalking, rust, corrosion and moisture

● Besides, it combines incredible hardness and bonding power to provide a heavy duty and to be used as topcoat.

PRODUCT ADVANTAGES

Extend the service life by 2-3 years

Resistance 98% sulfuric acid,30% hydrochloric acid carefree

Five years bright as new, 5.99% improve the yield of sensitive devices by 99%

50% Avoid slips and increase safety by 50%

这里可以自定义设置

PRODUCT PARAMETER

Mixingv	Ready to use
Thinner	Alkyd thinner
Airless spray	Nozzle tip: 0.017~0.023 inches Spray pressure: 15~18Mpa Thinner ratio: 5~15% (by weight of paint)
Brush, Roller	Recommended Must achieve required thickness

MORE SPECIFIC COLORS PLEASE CONSULT US

DRYING SCHEDULE

Substrate Temperature	10 ℃	20 ℃	30 ℃
To touch(40um)	5h	1h	30min
To handle(40um)	48h	24h	12h
Min. recoating time	36h	24h	12h

* Make sure no chalking and other contaminations before recoating

* Above data for reference only, actual drying time and recoating time is dependent on temperature, dry film thickness, ventilation conditions

PRODUCT SPECIFICATIONS

Color	Grey, flat gloss
Density, kg/L	~1.45
Volume solids	≥ 65%
Flash point, oC	35
Impact resistance, cm	50
Adhesion, MPa	≥ 6
Pot life, h	≥ 5

这里可以自定义设置

PRODUCT APPLICATION

Substrate temperature shall be at 3 ℃ higher than dew point, relative humidity less than 85%. Measurement of temperature and humidity should be close to substrate.