Hot Sale High Chlorinated Polyethylene Iron-red Primer for Steel Structure
PRODUCT DESCRIPTION
This product is composed of chlorosulfonated polyethylene, epoxy resin, plasticizer, iron oxide red, rust-resistant pigment, etc. It’s impressive that the coating can exceedingly resist rust, corrosion and water. Additionally, its fast-drying film has great hardness and strong adhesion.
Typical Uses:
This product can be applied as primer for steel structure suffering from chemical atmosphere and industrial air pollution. Meanwhile, it is suitable for the surface of concrete facilities.
Application Guide
● Mixing:
Use the power mixer to mix the main paint evenly.
● Mixing Ratio:
Ready to use
● Thinner:
Exclusive thinner.
● Airless Spray:
Nozzle tip: 0.018~0.025 inches.
Spray pressure: 15~18 MPa.
Thinner ratio: 5~15% (by weight of paint).
● Brush, Roller:
Recommended for small areas only.
Must achieve required thickness.
DRYING SCHEDULE
Substrate temperature | 10 °C | 20 °C | 30 °C |
To touch (40μm) | 5h | 1h | 0.5h |
To handle (40μm) | 48h | 24h | 12h |
| Min. recoating time | 12h | 4h | 2h |
* Make sure no chalking and other contaminations before recoating. | |||
* Above data for reference only, actual drying time and recoating time is dependent on temperature, dry film thickness, ventilation condition. | |||
SURFACE TREATMENT
All surfaces to be coated shall be clean and dry. The surface shall be evaluated and treated according to ISO8504 standard.
Bare steel: sandblasting to Sa2.5(IOS8501-1:2007). For the non-soaking site, acceptable for power tool grinding, at least reach St2(IOS8501-1:2007).
Painted surface: only apply to clean, dry and intact compatible primer.
APPLICATION
Application conditions: Substrate temperature shall be at 3℃ higher than dew point, relative humidity less than 85%. Measurement of temperature and humidity should be close to substrate.
CLASSICAL COATING SYSTEM
Please inquiry JIANBANG Paint for specific coating solutions.
High Chlorinated
Polyethylene Iron-red Primer : 2*30µm (dry film thickness)
High Chlorinated
Polyethylene Mica Iron Oxide Red Primer : 2*40µm (dry film thickness)
High Chlorinated
Polyethylene Finish : 2*30µm (dry film thickness)
SAFETY AND HEALTH
Please refer to MSDS before using this product. If you do not fully understand the restrictions, or cannot follow MSDS directions strictly, do not use this product. This volatile product is flammable. Keep this product away from flame or fire. Smoking is strictly prohibited in working area. Keep working area ventilated during application to make sure solvent vapor content is low in the air. PPE is necessary to avoid this product contacting with eyes or skin. More detailed safety tips are based on practical situation.
Please handle used paint barrel correctly to avoid any pollution.
Storage:
Store this product in shady, dry, ventilated and away from heat sources warehouse. Storage temperature above 0℃, the shelf life is 12 months at room temperature. If exceeding shelf life, the products shall be tested before using.
Disclaimer:
All technical data given in this document is based on our knowledge achieved in lab and practice, it is not completely correct. Although we try to keep the validity of our advice, however we cannot predict the practical conditions that will affect paint quality. Herein, we cannot be responsible for the consequences of variations in such conditions, or for unforeseen conditions. We reserve the right to modify this document without informing in advance.
Packaging | Packing size | Packing weight |
Part A | 20L | 25 KG |