Inorganic Zinc Silicate Heat Resist Primer Heat Treated Spray Paint
PRODUCT DESCRIPTION
This two-component product, which has strong resistance to rapid temperature change, oxidation and chemical corrosion, is mainly prepared by organic silicone resin, high temperature resistant pigments, aluminum paste and organic solvent. Moreover, the main advantage of this product is its excellent resistance to high temperature.
Typical Uses:
It is mainly designed as supporting primer for the anti-corrosion coating under 500℃. Metallurgical, petroleum, chemical and aviation industry are suitable as well.
Application Guide
● Mixing:
Use the power mixer to mix the main paint evenly, and then as you stir it, you add the hardener until you get to mix well. Generally, if the temperature below 10 ℃, it needs 30 min induction time; if the temperature over 10℃, it needs 15 min induction time.
● Airless Spray:
Part A: Part B= 30:3 (by weight).
● Thinner:
Inorganic high temperature resistance exclusive thinner.
● Airless Spray:
Nozzle tip：0.017~0.023 inch.
Spray pressure：15~18 MPa.
Thinner ratio：5~15% (by weight of paint).
● Spray, brush, roller:
Recommended must achieve required thickness.
DRYING SCHEDULE
Substrate temperature | 10 °C | 20 °C | 30 °C |
To touch (20μm) | 1h | 0.5h | 0.2h |
To handle (20μm) | 24h | 12h | 6h |
Min. recoating time | 8h | 4h | 2h |
Max. recoating time | 5h | 3h | 2h |
Pot Life | 4h | 2h | 1h |
* Make sure no chalking and other contaminations before recoating. | |||
* Above data for reference only, actual drying time and recoating time is dependent on temperature, dry film thickness, ventilation conditions. | |||
SURFACE TREATMENT
All surface to be coated shall be clean and dry. The surface shall be evaluated and treated according to ISO8504 standard.
Steel: Sanding to Sa2.5 (ISO8501-1:2007). It is acceptable to polish by power tools to meet at least St2.0(ISO8501-1:2007).
APPLICATION
Application conditions: Substrate temperature shall be at 3 °C higher than dew point, relative humidity less than 85%. Measurement of temperature and humidity should be close to substrate.
CLASSICAL COATING SYSTEM
Please inquiry JIANBANG paint for specific coating solutions.
Inorganic Zinc Silicate Heat Resist Primer: 2*30µm (dry film thickness)
Organic Silicone High Temperature Paint: 2*25µm (dry film thickness)
SAFETY AND HEALTH
Please refer to MSDS before using this product. If you do not fully understand the restrictions, or cannot follow MSDS directions strictly, do not use this product. This volatile product is flammable. Keep this product away from flame or fire. Smoking is strictly prohibited in working area. Keep working area ventilated during application to make sure solvent vapor content is low in the air. PPE is necessary to avoid this product contacting with eyes or skin. More detailed safety tips are based on practical situation.
Please handle used paint barrel correctly to avoid any pollution.
Storage:
Store this product in shady, dry, and ventilated warehouse. Storage temperature should be above 0℃. The shelf life is 12 months at room temperature. If exceeding shelf life, the products shall be tested before using.
Disclaimer:
All technical data given in this document is based on our knowledge achieved in lab and practice, it is not completely correct. Although we try to keep the validity of our advice, however we cannot predict the practical conditions that will affect paint quality. Herein, we cannot be responsible for the consequences of variations in such conditions, or for unforeseen conditions. We reserve the right to modify this document without informing in advance.
Packaging | Packing size | Packing weight |
Part A | 20L | 30 KG |
Part B | 4L | 3 KG |