PRODUCT DESCRIPTION

Acrylic polyurethane finish is a two-component high gloss finish based on aliphatic isocyanates and hydroxyl resins. Its strong weather resistance makes it able to retain its gloss and color against severe weather conditions. Furthermore, it also has the advantages of strong adhesion, anti-corrosion, rust resistance. What’s more, it is able to be re-coated for a long time.

Typical Uses:

This product, as coating for newly-constructed facilities and for their maintenance, can be matched with most epoxy resin-based paints in various environmental conditions, including marine environment, chemical and petrochemical environment. Besides, it is also suitable for the electric power industry, paper industry, vehicle, ships and so on. The traditional spraying method is recommended to obtain the best luster and appearance.

这里可以自定义设置

PRODUCT SELLING POINT

● Nanotechnology, compact structure.

● Salt spray corrosion resistance ≥3000h,Resistance to aging≥5000h.

● 98% concentrated sulfuric acid for 1200h.

● Resistance to 30% hydrochloric acid for 1200h.

●Factory direct sale.

PRODUCT ADVANTAGES

Repair rate 0, no downtime cost.Acceptance of all.

Extend the preservative time by 2.5 times.

Qualified for export of hazardous chemicals.

Performance and color optimization customization

这里可以自定义设置

PRODUCT APPLICATION GUIDE

Mixing	Use the power mixer to mix the main paint evenly, and then add the hardener and stir until it is well mixed.
Thinner	Acrylic polyurethane thinner
Mixing ratio	Part A: Part B = 20:4(by weight)
Airless spray	Nozzle tip: 0.017~0.023inches Spray pressure: 15~18Mpa Thinner ratio:0~15% (by weight of paint)
Brush, Roller	Recommended Must achieve required thickness.

MORE SPECIFIC COLORS PLEASE CONSULT US

DRYING SCHEDULE

Substrate Temperature	10 ℃	20 ℃	30 ℃
To touch(30um)	5h	2.5h	1.5h
To handle(30um)	20h	8h	4h
Min. recoating time	20h	8h	4h
Max. recoating time	4h	2h	1h

* Make sure no chalking and other contaminations before recoating. If necessary, stucco thoroughly before coating.

* Above data for reference only, actual drying time and recoating time is dependent on temperature, dry film thickness, ventilation conditions, humidity, mechanical strength, etc.

PRODUCT SPECIFICATIONS

Color	Customized
Gloss	High gloss
Density	~1.3Kg/L(after mixing)
Hardness	Polyurethane curing agent
Solid Volume	(50±2 )%
Standard Film thickness	60um dry film thickness (about 120um wet film thickness)
Theoretical spreading rate	6.4m²/Kg (60um dry film thickness)
Full cure	7d
Flash point	33℃

这里可以自定义设置

PRODUCT APPLICATION

Substrate temperature shall be at 3 ℃ higher than dew point, relative humidity less than 80%. Measurement of temperature and humidity should be close to substrate.