China Professional Chlorinated Rubber Aerial Sign Paint Factory...

这里可以自定义设置

PRODUCT DESCRIPTION

This product is composed of synthetic resin, chlorinated rubber, lightfast filler, plasticizer, etc. Meanwhile, the paint film has bright color, long weather resistance, excellent protection and decoration.

Typical Uses:

This product can be used as aerial sign paint for high-altitude buildings, steel and concrete chimneys. Besides, it is also designed for protection and decoration of other superstructure of ship hull.

这里可以自定义设置

PRODUCT SELLING POINT

● Repair rate 0, no downtime cost.

● The coating structure is designed independently.

● Performance and color optimization customization.

● Provide construction plan and construction service.

● The contract is guaranteed for 20 years.

PRODUCT ADVANTAGES

Repair rate 0,no downtime cost

Acceptance of all

Extend the presservative time by 2.5 times

Save 250% maintenance cost

这里可以自定义设置

PRODUCT APPLICATION GUIDE

Mixing	Ready to use
Thinner	Chlorinated rubber paint special thinner
Airless spray	Nozzle tip：0.017~0.023inch Spray pressure：15~18MPa Thinner ratio：0~15% (by weight of paint)
Brush、Roller	Recommended. Must achieve required thickness.

MORE SPECIFIC COLORS PLEASE CONSULT US

DRYING SCHEDULE

Substrate Temperature	10 ℃	20 ℃	30 ℃
To touch(50um)	2h	1h	30min
To handle(50um)	8h	4h	3h
Min. recoating time	8h	4h	3h
Max. recoating time	-	-	-

* Make sure no chalking and other contaminations before recoating.

* Above data for reference only, actual drying time and recoating time is dependent on temperature, dry film thickness, ventilation conditions.

PRODUCT SPECIFICATIONS

Color	Bright red, white
Gloss	Flat
Density	-1.41Kg/L
Solid Volume	(44±2 )%
Film thickness	100µm dry film thickness (about 220µm wet film thickness)
Theoretical spreading rate	3.1m²/Kg(60µm dry film thickness)
Flash point	31℃

这里可以自定义设置

PRODUCT APPLICATION

Substrate temperature shall be at 3^oC higher than dew point, relative humidity less than 85%. Measurement of temperature and humidity should be close to substrate.