Heat Resistant Paint

这里可以自定义设置

PRODUCT DESCRIPTION

The two-component paint is mainly based on silicon resin, special temperature-resistant

and corrosion-resistant pigment and curing agent. It can be used as primer and topcoat.

Moreover, this product has excellent resistance to heat, corrosion, oxidation and high

temperature. This paint can withstand 600 ℃ for a long time

Typical Uses:

This product is widely used for high temperature mark coating such as metallurgical, petroleum , chemical , aviation industry and etc. Also,it can be anticorrosive primer for structural steel with good impact and abrasion resistance

这里可以自定义设置

PRODUCT SELLING POINT

● Repair rate 0, no downtime cost.

● The coating structure is designed independently.

● Performance and color optimization customization.

● Provide construction plan and construction service.

● The contract is guaranteed for 20 years.

PRODUCT ADVANTAGES

Repair rate 0, no downtime cost

Acceptance of all

Extend the preservative time by 2.5 times

Save 250% maintenance cost

这里可以自定义设置

PRODUCT APPLICATION GUIDE

Mixing	Use the power mixer to mix the main paint evenly, and then as you stir it, you add the hardener until you get to mix well.
Mixing Ratio	Part A: Part B= 10:1 (by weight)
Thinner	High temperature resistance exclusive thinner
Airless spray	Nozzle tip：0.017~0.023inch Spray pressure：15~18MPa Thinner ratio：0~15% (by weight of paint)
Brush、Roller	Recommended for small areas only. Must achieve required thickness.
Roller coater	Not recommended.

MORE SPECIFIC COLORS PLEASE CONSULT US

DRYING SCHEDULE

Substrate Temperature	10 ℃	20 ℃	30 ℃
To touch(25um)	4h	2h	1h
To handle(25um)	24h	12h	6h
Min. recoating time	16h	8h	4h
Max. recoating time	10d	7d	5d
Use time after mixing	4h	2h	1h

* Make sure no chalking and other contaminations before recoating.

* Above data for reference only, actual drying time and recoating time is dependent on temperature, dry film thickness, ventilation conditions,humidity, mechanical strength, etc.

Color	Customized
Gloss	Flat
Density	-1.36Kg/L(after mixing)
Hardeness	Silicone curing agent
Solid Volume	(44±2 )%
Standard Film thickness	50µm dry film thickness (about 114µm wet film thickness)
Theoretical spreading rate	6.47m²/Kg(50µm dry film thickness)
Full cure	(23±2℃) 7d
Flash point	27℃

这里可以自定义设置

Substrate temperature shall be 3 ℃ higher than dew point with relative humidity below 85%. Measurement of temperature and humidity should be conducted close to substrate.