Oem Epoxy Mica Iron Oxide Intermediate Paint Marine Anti Corrosion...

这里可以自定义设置

PRODUCT DESCRIPTION

The two-component high-solid product is composed of epoxy resin and polyamie curing agent. Meanwhile, it is provided with great physical performance such as strong adhesion, flexibility, anti-abrasion, and anti-impact. Significantly, with low VOC, the coating has special performance in resisting water, alkali, oil, and chemicals.

Typical Uses:

This product is suitable for various environment such as marine facilities, petrochemical plant, bridges, pulp mill, etc. Meanwhile, it can be used as the intermediate paint in the epoxy coating system for concrete protection.

这里可以自定义设置

PRODUCT SELLING POINT

● Nanotechnology, compact structure.

● Salt spray corrosion resistance ≥3000h,Resistance to aging≥5000h.

● 98% concentrated sulfuric acid for 1200h.

● Resistance to 30% hydrochloric acid for 1200h.

●Factory direct sale.

PRODUCT ADVANTAGES

Repair rate 0, no downtime cost.Acceptance of all.

Extend the preservative time by 2.5 times.

Qualified for export of hazardous chemicals.

Performance and color optimization customization

这里可以自定义设置

PRODUCT APPLICATION GUIDE

Mixing	Use the power mixer to mix the main paint evenly, and then as you stir it, you add the hardener until you get to mix well. Generally, if the temperature below 10 ℃, it needs 30 min induction time; if the temperature over 10℃, it needs 15 min induction time.
Thinner	Epoxy paint thinner
Mixing ratio	Part A: Part B = 24:4
Airless spray	Nozzle tip: 0.018~0.027inches Spray pressure: 15~18Mpa Thinner ratio: 5~15% (by weight of paint)
Brush, Roller	Recommended Must achieve required thickness.

MORE SPECIFIC COLORS PLEASE CONSULT US

DRYING SCHEDULE

Substrate Temperature	10 ℃	20 ℃	30 ℃
To touch(75um)	4h	2h	1h
To handle(75um)	48h	24h	16h
Min. recoating time	56h	6h	4h
Max. recoating time	60d	30d	30d
Pot life	6h	4h	2h

* Make sure no chalking and other contaminations before recoating. If necessary, stucco thoroughly before coating.

* Above data for reference only, actual drying time and recoating time is dependent on temperature, dry film thickness, ventilation conditions, humidity, mechanical strength, etc.

PRODUCT SPECIFICATIONS

Color	Gray, Bronzing
Gloss	Flat
Density	~1.6Kg/L(after mixing)
Hardness	Curing agent for epoxy paint
Solid Volume	(75±2 )%
Standard Film thickness	150um dry film thickness (about 200um wet film thickness)
Theoretical spreading rate	3.13m²/Kg (150um dry film thickness)
Full cure	(23±2℃) 7d
Flash point	39℃

这里可以自定义设置

PRODUCT APPLICATION

Substrate temperature shall be 3 ℃ higher than dew point with relative humidity below 85%. Measurement of temperature and humidity should be conducted close to substrate.