Top Quality Cold Galvanizing Paint Factory

这里可以自定义设置

PRODUCT DESCRIPTION

This product is a new environmental friendly heavy-duty anti-corrosive coating composed of metal zinc, composite high corrosive-resistant film-forming material and active assistant. It has strong adhesion and is resistant to rust, salt and fog. The most impressing advantage of this product is that it has high zinc content--the zinc content of the formed film is over 96%, providing excellent cathodic protection and decoration, extraordinary weather-resistance and UV resistant ability.

Typical Uses:

This product can provide long-term protection as a primer or independent protective coating for internal and external surfaces of offshore and onshore steel structures. It can be used as an alternative to hot-dip galvanizing or hot spraying zinc(aluminum).

这里可以自定义设置

PRODUCT SELLING POINT

● Repair rate 0, no downtime cost.

● The coating structure is designed independently.

● Performance and color optimization customization.

● Provide construction plan and construction service.

● The contract is guaranteed for 20 years.

PRODUCT ADVANTAGES

Repair rate 0,no downtime cost

Acceptance of all

Extend the presservative time by 2.5 times

Save 250% maintenance cost

这里可以自定义设置

PRODUCT APPLICATION GUIDE

Mixing	Ready to use
Thinner	Special thinner for cold galvanizing paint
Airless spray	Nozzle tip: 0.025~0.031 inches Spray pressure: 18~28Mpa Thinner ratio: 5~15% (by weight of paint)
Brush、Roller	Recommended Must achieve required thickness

MORE SPECIFIC COLORS PLEASE CONSULT US

DRYING SCHEDULE

Substrate Temperature	10 ℃	20 ℃	30 ℃
To touch(40um)	4h	2h	1h
To handle(40um)	24h	12h	6h
Min. recoating time	16h	8h	4h
Max. recoating time	10d	7d	5d

* Make sure no chalking and other contaminations before recoating.

* Above data for reference only, actual drying time and recoating time is dependent on temperature, dry film thickness, ventilation conditions,humidity, mechanical strength, etc.

PRODUCT SPECIFICATIONS

Color	zinc gray
Gloss	No gloss
Density	-2.75Kg/L(after mixing)
Solid Volume	(45±2 )%
Standed Film thickness	80µm dry film thickness (about 178µm wet film thickness)
Theoretical spreading rate	2m²/Kg(80µm dry film thickness)
Full Cure	(23±2℃) 24h
Flash point	33℃

这里可以自定义设置

PRODUCT APPLICATION

Substrate temperature shall be 3 ℃ higher than the dew point, relative humidity less than 85%. Measurement of temperature and humidity should be close to substrate.