Alkyd Red Lead Anti-rust Primer

这里可以自定义设置

PRODUCT DESCRIPTION

This product is composed by grinding alkyd resin, red lead powder, extender pigment, drier and organic solvent. Significantly, it is provided with excellent performance in rust-resistance and film hardness. Besides, compared with oil-based red lead paint, this coating is more fast-drying. Furthermore, it has low requirements for rust removal.

Typical Uses:

This product can be applied as rust-resistant primer for ferrous metal such as bridges, steel structures, iron towers, vehicles, etc.

这里可以自定义设置

PRODUCT SELLING POINT

● The epoxy floor paint is mainly prepared by epoxy resin, curing agent, dispersant and aggregates depend on requirements.

● Main advantages of this paint are great resistance of slippery, electrostatic, acid and alkali.

● Moreover, it also has good resistance to organic solvent, heavy load and abrasion.

● Besides, it combines incredible hardness and bonding power to provide a heavy duty and to be used as topcoat.

PRODUCT ADVANTAGES

Extend the service life by 2-3 years

Resistance (chemical medium) 98% sulfuric acid, 30% hydrochloric acid carefree

Five years bright as new, 5.99% Improve the yield of sensitive devices by 99%

50% Avoid slips and increase safety by 50%

这里可以自定义设置

PRODUCT PARAMETER

Mixingv	Ready to use
Thinner	Exclusive thinner for alkyd paint
Airless spray	Nozzle tip: 0.017~0.023 inches Spray pressure: 15~18Mpa Thinner ratio: 5~15% (by weight of paint)
Brush, Roller	Recommended Must achieve required thickness

MORE SPECIFIC COLORS PLEASE CONSULT US

DRYING SCHEDULE

Substrate Temperature	10 ℃	20 ℃	30 ℃
To touch	8h	4h	3h
To handle	48h	24h	24h
Min. recoating time	36h	24h	24h

* Make sure no chalking and other contaminations before recoating

* Above data for reference only, actual drying time and recoating time is dependent on temperature, dry film thickness, ventilation conditions

PRODUCT SPECIFICATIONS

Color	Orange
Gloss	Flat
Density	~1.4Kg/L
Solid Volume	(40±2 )%
Standard Film thickness	80um dry film thickness (about 200um wet film thickness)
Theoretical spreading rate	3.57m²/Kg (80um dry film thickness)
Flash Point	38 ℃

这里可以自定义设置

PRODUCT APPLICATION

Substrate temperature shall be at 3 ℃ higher than dew point, relative humidity less than 85%. Measurement of temperature and humidity should be close to substrate.