Best Polyurethane Waterproof Paint Oem With Good Price

这里可以自定义设置

PRODUCT DESCRIPTION

This product is a two-component waterproof coating composed of isocyanate and hydroxyl resin. Meanwhile, it has excellent water resistance, weather resistance, light retention and long-term recoating.

Typical Uses:

As a new facility paint and maintenance finish, this paint can be used with most epoxy coating systems. It is widely applicable to a variety of environmental conditions, such as external walls of buildings, pools, bridges, offshore structures, etc.

这里可以自定义设置

PRODUCT SELLING POINT

● Long-Term recoating

● Excellent water resistance

● Excellent Light preservation

● Excellent weather resistance

● The contract is guaranteed for 20 years.

PRODUCT ADVANTAGES

Excellent water resistance,weather resistance

Save 250% maintenance coast

Widely applicable to a variety of environmental conditions

Light retention and long-term recoating

这里可以自定义设置

PRODUCT APPLICATION GUIDE

Mixing	Use the power mixer to mix the main paint evenly, and then as you stir it, you add the hardener until you get to mix well.
Thinner	Acrylic paint thinner
Airless spray	Nozzle tip：0.017~0.023inch Spray pressure：15~18MPa Thinner ratio：0~10% (by weight of paint)
Brush、Roller	Recommended Must achieve required thickness.

MORE SPECIFIC COLORS PLEASE CONSULT US

DRYING SCHEDULE

Substrate Temperature	10 ℃	20 ℃	30 ℃
To touch(50um)	2h	1h	30min
To handle(50um)	8h	4h	3h
Min. recoating time	8h	4h	3h
Max. recoating time	-	-	-

* Make sure no chalking and other contaminations before recoating.

* Above data for reference only, actual drying time and recoating time is dependent on temperature, dry film thickness, ventilation conditions.

PRODUCT SPECIFICATIONS

Color	Yellow, red, white
Gloss	Glossy
Density	-1.3Kg/L(after mixing)
Solid Volume	(50±2 )%
Film thickness	100µm dry film thickness (about 200µm wet film thickness)
Theoretical spreading rate	3.84m²/Kg(50µm dry film thickness)
Full cure	(23±2℃)24h
Flash point	25℃

这里可以自定义设置

PRODUCT APPLICATION

Substrate temperature shall be at 3^oC higher than dew point, relative humidity less than 85%. Measurement of temperature and humidity should be close to substrate.