Chlorinated Rubber Coating Primer For Metal Surfaces

这里可以自定义设置

PRODUCT DESCRIPTION

This rust-resistant paint, based on chlorinated rubber resin, has excellent performance in adhesion to steel, corrosion-resistance, and low-temperature construction property. Moreover, its film is free from saponification.

Typical Uses:

This product can be applied as rust-resistant primer for ship bottom, steel structure below waterline in various environment.

这里可以自定义设置

PRODUCT SELLING POINT

● The epoxy floor paint is mainly prepared by epoxy resin, curing agent, dispersant and aggregates depend on requirements.

● Main advantages of this paint are great resistance of slippery, electrostatic, acid and alkali.

● Moreover, it also has good resistance to organic solvent, heavy load and abrasion.

● Besides, it combines incredible hardness and bonding power to provide a heavy duty and to be used as topcoat.

PRODUCT ADVANTAGES

Extend the service life by 2-3 years

Resistance (chemical medium) 98% sulfuric acid, 30% hydrochloric acid carefree

Five years bright as new, 5.99% Improve the yield of sensitive devices by 99%

50% Avoid slips and increase safety by 50%

这里可以自定义设置

PRODUCT PARAMETER

Mixingv	Ready to use
Thinner	Chlorinated rubber thinner
Airless spray	Nozzle tip: 0.018~0.025 inches Spray pressure: 18~25Mpa Thinner ratio: 5~15% (by weight of paint)
Brush, Roller	Recommended Must achieve required thickness

MORE SPECIFIC COLORS PLEASE CONSULT US

DRYING SCHEDULE

Substrate Temperature	10 ℃	20 ℃	30 ℃
To touch(50um)	3h	2h	1h
To handle(50um)	48h	24h	12h
Min. recoating time	12h	6h	3h

* Make sure no chalking and other contaminations before recoating

* Above data for reference only, actual drying time and recoating time is dependent on temperature, dry film thickness, ventilation conditions

PRODUCT SPECIFICATIONS

Color	Customized
Gloss	Semi-gloss
Density	~1.4Kg/L
Solid Volume	(42±2 )%
Standard Film thickness	100um dry film thickness (about 238um wet film thickness)
Theoretical spreading rate	3m²/Kg (100um dry film thickness)
Flash Point	31 ℃

这里可以自定义设置

PRODUCT APPLICATION

Substrate temperature shall be at 3 ℃ higher than dew point, relative humidity less than 85%. Measurement of temperature and humidity should be close to substrate.