Chlorosulfonated Polyethylene Anti-corrosive Intermediate Paint...

这里可以自定义设置

PRODUCT DESCRIPTION

The product is composed of the chlorosulfonated polyethylene rubber. Meanwhile, it contains the modified resin, leveling agent and anti-sinking agent. Besides, this paint also has the organic solvent, curing agent, flake anti-rust pigment, etc. Furthermore, this coating has excellent shielding, bottom contact, strong adhesion and thick film. What’s more, it can reduce the construction time and is easy to construct.

Typical Uses:

This product can be used as an intermediate paint of anti-corrosion coating.

这里可以自定义设置

PRODUCT SELLING POINT

● The epoxy floor paint is mainly prepared by epoxy resin, curing agent, dispersant and aggregates depend on requirements.

● Main advantages of this paint are great resistance of slippery, electrostatic, acid and alkali.

● Moreover, it also has good resistance to organic solvent, heavy load and abrasion.

● Besides, it combines incredible hardness and bonding power to provide a heavy duty and to be used as topcoat.

PRODUCT ADVANTAGES

Extend the service life by 2-3 years

Resistance (chemical medium) 98% sulfuric acid, 30% hydrochloric acid carefree

Five years bright as new, 5.99% Improve the yield of sensitive devices by 99%

50% Avoid slips and increase safety by 50%

这里可以自定义设置

PRODUCT PARAMETER

Mixingv	Use the power mixer to mix the main paint evenly, and then as you stir it, you add the hardener until you get to mix well.
Mixing ratio	Part A: Part B= 20:4 (by weight)
Thinner	Special thinner
Airless spray	Nozzle tip: 0.018~0.025 inches Spray pressure: 18~25Mpa Thinner ratio: 5~15% (by weight of paint)
Brush、Roller	Recommended Must achieve required thickness

MORE SPECIFIC COLORS PLEASE CONSULT US

DRYING SCHEDULE

Substrate Temperature	10 ℃	20 ℃	30 ℃
To touch(30µm)	2.5h	1h	0.5h
To handle(30µm)	48h	24h	12h
Min. recoating time	12h	4h	2h
Max. recoating time	-	-	-
Pot life	6h	4h	2h

* Make sure no chalking and other contaminations before recoating

* Above data for reference only, actual drying time and recoating time is dependent on temperature, dry film thickness, ventilation conditions

PRODUCT SPECIFICATIONS

Color	Brown, Gray
Gloss	Semi-gloss
Density	~1.55 Kg/L
Solid Volume	(52±2)%
Standard Film thickness	80um dry film thickness (about 145um wet film thickness)
Theoretical spreading rate	4.2m²/Kg(80µm dry film thickness)
Flash Point	31℃

这里可以自定义设置

PRODUCT APPLICATION

Substrate temperature shall be at 3 ℃ higher than dew point, relative humidity less than 85%. Measurement of temperature and humidity should be close to substrate.