Epoxy Glass Flakes Anti-rust Paint Exceedingly Withstand Water And Chemicals...

这里可以自定义设置

PRODUCT DESCRIPTION

This two-component thick film coating is composed of epoxy resin, amine adduct curing agent, glass flakes, pigment, etc. Significantly, its film has excellent impermeability, strong adhesion and high mechanical strength. Besides, it also has great resistance to abrasion, cracks, vibrations. Furthermore, this paint can exceedingly withstand water and chemicals, with long-term anti-corrosion performance.

Typical Uses:

This product is used as the heavy anti-corrosion coating for marine engineering facilities, offshore platforms, oil pipelines, and large-scale penstocks of hydroelectric stations. Meanwhile, it is also suitable for bridges, gates, gas cabinets, buried pipelines, etc.

这里可以自定义设置

PRODUCT SELLING POINT

● Nanotechnology, compact structure.

● Salt spray corrosion resistance ≥3000h,Resistance to aging≥5000h.

● 98% concentrated sulfuric acid for 1200h.

● Resistance to 30% hydrochloric acid for 1200h.

●Factory direct sale.

PRODUCT ADVANTAGES

这里可以自定义设置

PRODUCT APPLICATION GUIDE

Mixing	Use the power mixer to mix the main paint evenly, and then as you stir it , you add the hardener until you get to mix well
Thinner	Exclusive epoxy paint thinner Thinner ratio: 0%~15% (by weight of paint)
Mixing ratio	Part A: Part B = 20:5
Airless spray	Nozzle tip: 0.018~0.027inches Spray pressure: 15~18Mpa Thinner ratio: 5~15% (by weight of paint)
Brush, Roller	Recommended Must achieve required thickness.

DRYING SCHEDULE

Substrate Temperature	10 ℃	20 ℃	30 ℃
To touch(50um)	7h	4h	3h
To handle(50um)	48h	48h	48h
Min. recoating time	11h	6h	4h
Max. recoating time	15d	10d	7d
Pot life	6h	4h	2h

* Make sure no chalking and other contaminations before recoating. If necessary, stucco thoroughly before coating.

* Above data for reference only, actual drying time and recoating time is dependent on temperature, dry film thickness, ventilation conditions, humidity, mechanical strength, etc.

PRODUCT SPECIFICATIONS

Color	Iron-red, Gray, Black
Gloss	Matte, Flat
Density	~1.4Kg/L(after mixing)
Solid Volume	(60±2 )%
Standard Film thickness	100um dry film thickness (about 167um wet film thickness)
Theoretical spreading rate	4.28m²/Kg (100um dry film thickness)
Full cure	(23±2℃) 7d
Flash point	38℃

这里可以自定义设置

PRODUCT APPLICATION

Substrate temperature shall be 3 ℃ higher than dew point with relative humidity below 85%. Measurement of temperature and humidity should be conducted close to substrate.