Epoxy Mica Iron Oxide Intermediate Paint

这里可以自定义设置

PRODUCT DESCRIPTION

The two-component high-solid product is composed of epoxy resin and polyamie curing agent. Meanwhile, it is provided with great physical performance such as strong adhesion, flexibility, anti-abrasion, and anti-impact. Significantly, with low VOC, the coating has special performance in resisting water, alkali, oil, and chemicals.

Typical Uses:

This product is suitable for various environment such as marine facilities, petrochemical plant, bridges, pulp mill, etc. Meanwhile, it can be used as the intermediate paint in the epoxy coating system for concrete protection.

这里可以自定义设置

PRODUCT SELLING POINT

● The epoxy floor paint is mainly prepared by epoxy resin, curing agent, dispersant and aggregates depend on requirements.

● Main advantages of this paint are great resistance of slippery, electrostatic, acid and alkali.

● Moreover, it also has good resistance to organic solvent, heavy load and abrasion.

● Besides, it combines incredible hardness and bonding power to provide a heavy duty and to be used as topcoat.

PRODUCT ADVANTAGES

Extend the service life by 2-3 years

Resistance (chemical medium) 98% sulfuric acid, 30% hydrochloric acid carefree

Five years bright as new, 5.99% Improve the yield of sensitive devices by 99%

50% Avoid slips and increase safety by 50%

这里可以自定义设置

PRODUCT PARAMETER

Mixingv	Use the power mixer to mix the main paint evenly, and then as you stir it, you add the hardener until you get to mix well. Generally, if the temperature below 10 ℃, it needs 30 min induction time; if the temperature over 10℃, it needs 15 min induction time.
Mixing ratio	Part A: Part B = 24:4 (by weight)
Thinner	Epoxy paint thinner
Airless spray	Nozzle tip: 0.018~0.027inches Spray pressure: 15~18Mpa Thinner ratio: 5~15% (by weight of paint)
Brush、Roller	Recommended Must achieve required thickness

MORE SPECIFIC COLORS PLEASE CONSULT US

DRYING SCHEDULE

Substrate Temperature	10 ℃	20 ℃	30 ℃
To touch(75um)	4h	2h	1h
To handle(75um)	48h	24h	16h
Min. recoating time	56h	6h	4h
Max. recoating time	60d	30d	30d
Pot life	6h	4h	2h

* Make sure no chalking and other contaminations before recoating

* Above data for reference only, actual drying time and recoating time is dependent on temperature, dry film thickness, ventilation conditions

PRODUCT SPECIFICATIONS

Color	Gray, Bronzing
Gloss	Flat
Density	~1.6Kg/L (after mixing)
Hardness	Curing agent for epoxy paint
Solid Volume	(75±2 )%
Standard Film thickness	150um dry film thickness (about 200um wet film thickness)
Theoretical spreading rate	3.13m²/Kg (150um dry film thickness)
Full cure	(23±2℃ )7d
Flash Point	39℃

这里可以自定义设置

PRODUCT APPLICATION

Substrate temperature shall be at 3 ℃ higher than dew point, relative humidity less than 85%. Measurement of temperature and humidity should be close to substrate.