Various Colors High Chlorinated Polythene Enamel

这里可以自定义设置

PRODUCT DESCRIPTION

This product is composed of high chlorinated polythene, special resin, plasticizer, pigment, auxiliary, etc. It has the advantages of strong weather-resistance, anti-aging ability, salt and fog resistance, as well as acid and alkali resistance. Besides, this product is also able to withstand chemical atmosphere, water, oil, heat and low temperature. The paint dries quickly and its film is firm, and be able to resist abrasion. In addition, it forms a thick film after one time application, and very easy for construction.

Typical Uses:

This product is widely used on steel structure equipment and facilities such as chemical pipes, pipelines, supports, plants, etc., as well as the outer wall of acid, alkali and salt storage tank for anti-corrosion purpose. It is commonly seen in metallurgy, petroleum, chemical industry and construction industry. What’s more, it is also suitable for seaport, wharf, energy and other industries.

这里可以自定义设置

PRODUCT SELLING POINT

● The epoxy floor paint is mainly prepared by epoxy resin, curing agent, dispersant and aggregates depend on requirements.

● Main advantages of this paint are great resistance of slippery, electrostatic, acid and alkali.

● Moreover, it also has good resistance to organic solvent, heavy load and abrasion.

● Besides, it combines incredible hardness and bonding power to provide a heavy duty and to be used as topcoat.

PRODUCT ADVANTAGES

Extend the service life by 2-3 years

Resistance (chemical medium) 98% sulfuric acid, 30% hydrochloric acid carefree

Five years bright as new, 5.99% Improve the yield of sensitive devices by 99%

50% Avoid slips and increase safety by 50%

这里可以自定义设置

PRODUCT PARAMETER

Mixingv	Ready to use
Thinner	Exclusive thinner for high chlorinated polythene
Airless spray	Nozzle tip: 0.017~0.023 inches Spray pressure: 15~18Mpa Thinner ratio: 0~15% (by weight of paint)
Brush, Roller	Recommended Must achieve required thickness

MORE SPECIFIC COLORS PLEASE CONSULT US

DRYING SCHEDULE

Substrate Temperature	10 ℃	20 ℃	30 ℃
To touch(30um)	4h	2h	1h
To handle(30um)	24h	12h	6h
Min. recoating time	16h	8h	4h
Max. recoating time	10d	7d	5d

* Make sure no chalking and other contaminations before recoating

* Above data for reference only, actual drying time and recoating time is dependent on temperature, dry film thickness, ventilation conditions

PRODUCT SPECIFICATIONS

Color	Customized
Gloss	Flat
Density	~1.4Kg/L
Solid Volume	(44±2 )%
Standard Film thickness	60um dry film thickness (about 136um wet film thickness)
Theoretical spreading rate	5.23m²/Kg (60um dry film thickness)
Flash Point	31℃

这里可以自定义设置

PRODUCT APPLICATION

Substrate temperature shall be at 3 ℃ higher than dew point, relative humidity less than 85%. Measurement of temperature and humidity should be close to substrate.